进口高强度板举例说明S690QL
- S = Structural Steel
- 690 = minimum yield strength (MPa)
- Q = Quenching & Tempering
- L = Low notch toughness testing temperature
Chemical Composition
| Grade | C | Si | Mn | P | S | N | B | Cr | Cu | Mo | Nb* | Ni | Ti* | V* | Zr* |
| S690QL | 0.20 | 0.80 | 1.70 | 0.025 | 0.015 | 0.015 | 0.0050 | 1.50 | 0.50 | 0.70 | 0.06 | 2.0 | 0.05 | 0.12 | 0.15 |
Mechanical Properties
| Designation | Mechanical Properties (ambient temperature) | |||||||
| Steel Name | Steel Number | Min. Yield Strength Reh MPa | Tensile Strength Rm MPa | Min. % elongation after fracture | ||||
| Nominal thickness (mm) | Nominal thickness (mm) | |||||||
| ≥3 ≤50 | ≥50 ≤100 | ≥100 ≤150 | ≥3 ≤50 | ≥50 ≤100 | ≥100 ≤150 | |||
| S690QL | 1.8931 | 690 | 650 | 630 | 770/940 | 760/930 | 710/900 | 14 |
V Notch Impact Testing
| Grade | Sample Orientation | @ 0°C | @-20°C | @-40°C | @-60°C |
| S690QL | Longitudinal | 50 J | 40 J | 30 J | –– |
| Traverse | 35 J | 30 J | 27 J | –– |